Capacitor and production method therefor

ABSTRACT

A solid electrolytic capacitor is obtained in which a sintered metal  11  is served as an anode and a silver layer is served as a cathode. The surface of sintered metal made of tantalum or the like and having an open porosity ratio of more than 75% is oxidized so as an oxide film  12  made of tantalum pentoxide or the like is deposited thereon. The cavities of the metal are filled with an electrically conductive material  13 . Then the metal is wound around a lead wire and made into a desired shape and size. The silver layer is formed on the porous metal body. Because the surface area ratio of the sintered metal is large, a large capacity is obtained.

TECHNICAL FIELD

[0001] The present invention relates to a capacitor used in a variety of electronic devices such as personal computers, and a method of manufacturing the capacitor.

BACKGROUND ART

[0002] As an example of a conventional capacitor, a tantalum solid electrolytic capacitor is described below.

[0003]FIG. 3 is a cross-sectional view of the conventional tantalum solid electrolytic capacitor. A tantalum lead wire 1 and a sintered body 2 produced by sintering a mass of molded tantalum powder are jointed together. A graphite layer 3 is formed on a surface of the sintered body 2, and a silver layer 4 is formed on outside the graphite layer 3. An electrode 5A is connected to the tantalum lead wire 1, and an electrode 5B is coupled to the silver layer 4. An electrode body thus produced is covered with a resin package 6.

[0004] A manufacturing method of the capacitor is demonstrated below.

[0005] First, mold a mass of tantalum powder placed around the lead wire 1 at high pressure, and sinter the molded powder to make the sintered body 2. Then, anode-oxidize the sintered body 2 in phosphoric acid solution, and produce a dielectric film of tantalum pentoxide on the surface of the body 2 (not illustrated). Next, fill cavities of the sintered body 2 with a solid-electrolyte of manganese-dioxide or the like (not illustrated), and successively form the graphite layer 4 and the silver layer 5 on the surface of the sintered body 2. Finally, connect the electrode 6A and the electrode 6B to the tantalum lead wire 1 and the silver layer 5 respectively, and cover an outside of the electrode body with the resin package 7.

[0006] The manufacturing method of the sintered body 2 used in the capacitor is disclosed in Japanese Patent Laid-Open Application No. S63-262833, as an example. More specifically, the method includes the steps of mixing camphor grains having a specified mean diameter with a metallic powder, press-molding the mixture and evaporating the camphor by heating. A porosity ratio of the sintered body is up to about 75%. Because the surface area of the dielectric film is small, a large capacity is hardly obtainable.

SUMMARY OF THE INVENTION

[0007] A capacitor of the present invention includes a sintered metal made of foam metal, and electrically conductive material which is placed on a surface of an oxide film of the sintered metal. The sintered metal has a skeleton of a solid construction and its porosity ratio is more than 75% and 97% or less. A manufacturing method of the capacitor includes steps of forming the conductive material on the surface of the oxide film which is deposited on the sintered metal, and forming the sintered metal into a desired shape and size.

BRIEF DESCRIPTOIN OF THE DRAWINGS

[0008]FIG. 1 is an ideational cross-sectional view of a porous body in accordance with a first and a second exemplary embodiment of the present invention.

[0009]FIG. 2 is a cross-sectional view of a capacitor in accordance with the first and the second exemplary embodiment of the present invention.

[0010]FIG. 3 is a cross-sectional view of a conventional capacitor.

DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS

[0011] First Exemplary Embodiment

[0012]FIG. 1 is an ideational cross-sectional view of a porous body in accordance with the first exemplary embodiment of the present invention. In FIG. 1, a sintered metal 11 is made of tantalum, which has a skeleton of a solid construction with a porosity ratio of more than 75% and 97% or less and a surface area ratio of 10,000 m²/m³ or more, and has an oxide film 12 of tantalum pentoxide on its surface. An electrically conductive material 13 fills open cavities of the metal and covers a surface of the oxide film 12. The conductive materials 13 are mutually connected (not shown).

[0013]FIG. 2 is a cross-sectional view of a capacitor produced by the porous body illustrated in FIG. 1. A sintered body 22 produced by sintering a mass of molded tantalum powder is jointed with a tantalum lead wire 21. A graphite layer 23 is formed on a surface of the sintered body 22, and a silver layer 24 is formed on outside the graphite layer. An electrode 25A is connected to the tantalum lead wire 21, and an electrode 25B is connected to the silver layer 24. An electrode body fabricated in this manner is covered with a resin package 26.

[0014] A manufacturing method of this capacitor is described below.

[0015] First, mix following materials to produce slurry;

[0016]1) tantalum powder of 30-80 weight %(wt %) and of an average particle diameter of 0.5-100 tm,

[0017]2) water-soluble binder of 2-10 wt % such as ethyl cellulose,

[0018]3) foaming agent of 0.5-5% and of a 5-8 C hydrocarbon organic solvent or the like,

[0019]4) anionic surfactant or nonionic surfactant of 0.5-3 wt %,

[0020]5) plasticizer of 2-10 wt % such as polyvinyl alcohol, and

[0021]6) a solvent such as water;

[0022] and maintain the slurry viscosity of 3,000-55,000 cps at 20° C.

[0023] Next, form a sheet of the slurry of a desired thickness on a mold release layer of a carrier-film using a doctor blade method.

[0024] Then, keep the sheet at 25-40° C. and 80% or more humidity, thereby preventing the surface from being cracked, and evaporating the foaming agent to form bubbles.

[0025] Then, cohere the slurry at a boundary between the bubbles by heating and drying the sheet at 40-80° C.

[0026] Then, separate the sheet from the carrier film and cut into a desired shape and size, degrease the cut sheet and sinter it. Degreasing and sintering under lower oxygen partial pressure than equilibrium oxygen partial pressure of the tantalum is desirable.

[0027] The sheet after sintering is the sintered metal 11 with a skeleton of a solid construction of 75.5% open porosity ratio and the surface area ratio of 10,000 m²/m³. Then, etch the surface of the metal 11 to further increase the surface area.

[0028] Next, produce the oxide film 12 of tantalum pentoxide on the surface of the sintered metal 11, by electro-chemically anode-oxidizing the metal 11 in a phosphoric acid solution. Then, fill out the cavities of the sintered metal 11 (the surface of the oxide film 12) with manganese dioxide, i.e., a solid electrolyte 13, which is hereafter called a porous body 22.

[0029] Then, wind the sheet of the porous body 22 around the tantalum lead wire 21 with compressing the sheet, and make a desired shape and size. At this time, electrically connect the sintered metal 11 composing the porous body 22 with the tantalum lead wire 21, by destroying an area of connection of the oxide film 12 mechanically or with large electricity and welding the metal 11 and the wire 21 together, for example. In a case the oxide film 12 is damaged at a boundary of the connection, reformation of the film 12 by an electrochemical method is desirable.

[0030] Next, apply a graphite paste to outside of the porous body 22, and dry to form the graphite layer 23. Successively, apply a silver paste to the layer and dry to form the silver layer 24. Connect the electrode 25A to the tantalum lead wire 21, and connect the electrode 25B to the silver layer 24, cover outside of the body with the resin package 26 to finally obtain the capacitor as illustrated in FIG. 2.

[0031] The open porosity rate of this capacitor is 75%. Because the sintered metal 11 has the high open porosity ratio in itself, it allows the oxide film to have a larger surface area per unit volume, thereby allowing the capacitor to have a large capacity. Furthermore, because the sintered metal 11 is cut into the desired shape and size after the cavities are filled with the conductive material 13, the cavities are effectively filled with the conductive material 13. Still furthermore, because the sheet is compressed when it is cut into the desired shape and size, surface area per unit volume of the oxide film 12 is enlarged, thereby making the capacitor having a larger capacity easily.

[0032] Second Exemplary Embodiment

[0033] The second exemplary embodiment differs from the first exemplary embodiment in an open porosity ratio of a sintered metal 11 and in an electrically conductive material 13. More specifically, in the second exemplary embodiment, composition, bubbling conditions and the like for making slurry are controlled as to obtain the open porosity ratio of 97%. Polypyrrole, i.e., a conductive polymer, is used for the electrically conductive material 13. The polypyrrole is filled as below. Immerse the sintered metal 11 coated with an oxide film 12 in a methanol solution of ferric dodecylbennzenesulfonate. Remove the body from the solution and dry, then successively immerse the body in pyrrole solution. After that, remove the body from the solution and dry again. With this chemical oxide polymerization, the polypyrrlole, i.e., a conductive polymer is filled into cavities of the sintered metal 11. Immersing the sintered metal 11 in the methanol solution and in the pyrrole solution in a vacuum or in a pressurized atmosphere helps the liquid penetrates easily into the sintered metal 11, and improve a filling efficiency of the conductive material 13.

[0034] Afterwards, by taking the same method used in the first exemplary embodiment, a capacitor illustrated in FIG. 2 is obtained.

[0035] A capacitor with a large capacity is obtained in the second exemplary embodiment as in the first exemplary embodiment. In the second exemplary embodiment, the sintered metal 11 coated with the oxide film 12 is immersed in the electrically conductive polymer solution so as the conductive material 13 is easily filled into the cavities. This method allows the conductive material 13 to cover a surface of the oxide film 12 easier than the first exemplary embodiment, so that a large capacity for the capacitor is ensured.

[0036] Moreover, because an electrical conductivity of the material 13 is higher than that of the manganese dioxide, the capacitor is given a lower resistance and faster response to high frequencies than the first exemplary embodiment.

[0037] In the first and the second exemplary embodiments, the sintered metal 11 made of the tantalum which has the open porosity ratio of 75%-97% and the surface area ratio of 10,000 m²/m³ or more is used. The higher the surface area ratio becomes, the larger the surface area of the oxide film 12 becomes, so the larger capacity is available. Therefore it is more desirable to provide the open porosity ratio of 90%-97%.

[0038] However, if the porosity ratio exceeds 97%, the metal density decreases and an electrostatic capacitance per unit volume is possibly reduced. From a point of the surface area, it is desirable to compress the porous body 22 for enlarging the surface area per unit volume of the oxide film 12 when the porous body 22 is wound around the tantalum lead wire 21. The porous body 22 without compressing is allowed, however, it is desirable to maintain the open porosity ratio of 75%-97% in any case.

[0039] The capacitor is similarly composed as long as the sintered metal 11 is composed of one or more of aluminum, niobium, titanium, hafnium, zirconium, zinc, tungsten, bismuth and antimony, as well as tantalum.

[0040] In addition, because the sintered metal 11 is cancellous and has a skeleton of a solid construction, the sintered metal 11 is so strong that the capacitor is allowed to have a high strength against impact.

[0041] Material, such as a solid electrolyte of the manganese dioxide, the conductive polymer such as the polypyrrole or a polyethylene-dioxythiophene, increases a contact area between the porous body 22 and the graphite layer 23. Thus, an equivalent resistance between the porous body 22 and the electrode 25B decreases, so that the capacitor having the large capacity and a high-quality is obtained.

[0042] Moreover, because the surface area of the sintered metal 11 is further expanded by etching, the surface area of the oxide film 12 is also expanded, so that the capacity is enlarged with it.

[0043] Still more, the present invention is not limited to the composition described in above exemplary embodiments. As long as the capacitor is composed of the sintered metal 11 served as the anode, the oxide film 12, which is deposited on the surface of the metal 11 and served as a dielectric layer, and a metal, which is formed on the surface of the oxide film 12 via the conductive material 13 and served as the cathode, the capacitor with large capacity can be similarly obtained.

[0044] The high-capacitance capacitor can be also obtained by using a tantalum foil instead of the tantalum lead wire 21, namely, compressing and bonding the sheet of the sintered metal 11 on both sides of the tantalum foil.

INDUSTRIAL APPLICABILITY

[0045] The present invention provides a capacitor with large capacity, by employing a sintered metal having a porosity ratio of 75-80% as an anode and depositing an oxide film on a surface of the metal. 

1. A capacitor comprising: a sintered metal made of a foam metal with a skeleton of a solid construction having an open porosity ratio of more than 75% and at most 97%, and having an oxide film on its surface; and an electrically conductive material formed on a surface of the oxide film of said sintered metal.
 2. The capacitor as defined in claim 1, wherein a surface area ratio of said sintered metal is at least 10,000 m²/m³.
 3. The capacitor as defined in claim 1, wherein said sintered metal includes at least one of aluminum, tantalum, niobium, titanium, hafnium, zirconium, zinc, tungsten, bismuth, and antimony.
 4. The capacitor as defined in claim 1, wherein said electrically conductive material is a solid electrolyte.
 5. The capacitor as defined in claim 1, wherein said electrically conductive material is an electrically conductive polymer.
 6. A method of manufacturing a capacitor comprising the steps of: (a) forming an electrically conductive material on a surface of an oxide film on a surface of a sintered metal made of a foam metal with a skeleton of a solid construction having an open porosity ratio of more than 75% and at most 97%, and (b) making said sintered metal into a desired shape and size.
 7. The method of manufacturing the capacitor as defined in claim 6 further comprising a step of: (c) etching the surface of said sintered metal.
 8. The method of manufacturing the capacitor as defined in claim 6, wherein step (b) includes: compressing said sintered metal. 